Heidelberg - Jena - St.Petersburg - Database of Optical Constants (HJPDOC)

M i s c e l l a n e o u s


state material data range (micron) reference (and link)
amor. CaCO3 transm. [fig] 2.5 - 30 Knacke, Kraetschmer (1980) Astron. Astrophys. 92, 281.
. FeSi cond.(T) [fig] 0.1 - 1000 Degiorge et al. (1994) Europhys. Lett. 28, 341
cryst. FeSi refl.(T) [fig] 0.1 - 1000 Paschen et al. (1997) Phys. Rev. B 56, 12916
. CaCO3 n,k [t+f] . Tropf (1998) in Palik E. (ed) Handbook of Optical Constants of Solids, III. Acad. Press, p.701
. FeSi abs. [fig] 26 - 55 Ferrarotti et al. (2000) Astron. Astrophys. 357, L13
. Mg2Si n,k [f+t] 0.05 - 0.2 Larruquert, Keski-Kuha (2000) Appl. Opt. 39, 2772
irrad. MgCO3 luminesc.sp. [fig] 0.3 - 0.9 Koike et al. (2002) Astron. Astrophys., in press.
. CaCO3 (calcite; limestone) n, k [fig], Cext/V (cm-1) [fig] 1.5 - 62.5 Jurewicz et al. (2003) A&A
. Ca(OH)2 (smoke grain) mass absorption coefficent k[cm2g-1][fig] 2.5-25 Kimura, Nuth (2005) ApJ
? Mg(OH)2 (Brucite)(synthetic)(thin & thick fimls) Absorbance [fig.] 2.5-200
50-650cm-1 (200-15)
450-4000cm-1 (23-2.5)
Hofmeister, Bowey (2006) MNRAS

Notes:
state: amor. - amorphous, cryst. - crystalline, glas. - glassy.
data: m.abs.c. - mass absorption coefficient, cond. - conductivity, n,k - refractive index; (T) - dependence on temperature; [fig] - figure, [tab] - table, (c!) - compilation.
Created by V.I., N.K. | Last Change: J.P. | Valid HTML 4.01! Valid CSS!

Last change: 20.03.2008